Ki sa ki fè 1235 alyaj patikilyèman apwopriye pou ityòm batri aktyèl pèseptè?
Alloy aliminyòm 1235 la (Al pi gran pase oswa egal a 99.35%) ofri balans optimal ant konduktiviti elektrik (pi gran pase oswa egal a 62% IACS) ak fòs mekanik (fòs rupture 80 - 120MPA). Iron kontwole li yo - Silisyòm rapò (Fe mwens pase oswa egal a 0.25%, Si mwens pase oswa egal a 0.65%) minimize korozyon elèktrochimik nan elektwolit òganik. Konpòtman inik alyaj la nan rkristalizasyon pandan rkwir asire ki konsistan plato papye (± 1mm/m). Konpare ak seri pi 1xxx, li bay 15-20% pi bon rezistans twou pou pwoteksyon separasyon. Karakteristik sa yo fè li chwa a pi pito pou wo-enèji dansite NMC batri katod.
Ki jan pwosesis la woule pou 1235 papye batri diferan de pwodiksyon papye konvansyonèl?
Precision Rolling Fwad anplwaye 20 - Segondè Cluster Mills reyalize Ultra - mezi mens (6 - 15μm) ak ± 0.5μm tolerans epesè. Entele entèmedyè nan 280 - 320 degre dispans travay redi pandan w ap kenbe O-temper tendres. Se fini sifas kontwole Ra 0.1-0.2μm lè l sèvi avèk woulo travay poli ak 0.05μm brutality. Pwosesis la gen ladan nan-liy lazè kontwole epesè chak 50mm nan longè papye. Pase final yo fèt nan vitès anba a 300m/min yo anpeche mikwo-krak fòmasyon nan mezi mens.
Ki sa ki teknoloji tretman sifas yo aplike nan 1235 papye pou pèfòmans batri amelyore?
Oksidasyon electrochemical kreye yon kouch 50-100nm pore oksid pou amelyore adezif lyezon. Tretman idrofil (ang kontak<30°) improves electrode slurry wettability during coating. Some manufacturers apply nano-silica coatings (3-5mg/m²) to reduce interface resistance. Edge insulation treatments use ceramic particles to prevent dendritic growth. These processes collectively increase cycle life by ≥500 cycles in 4.4V high-voltage applications.
Ki jan 1235 FOIL konpare ak 1060/1070 alyaj nan aplikasyon pou batri?
Pandan ke 1060/1070 ofri yon ti kras pi wo konduktiviti (1 - 2% avantaj IACS), 1235 bay pi bon formability (elongasyon pi gran pase oswa egal a 25% vs 20%). Kontwòl pi sere 1235 la (Cu mwens pase oswa egal a 0.02% vs 0.03%) diminye reyaksyon bò ak elektwolit LipF6. Rezistans ka zo kase li yo (Kic pi gran pase oswa egal a 18MPa · m½) se 30% pi wo pase 1070 nan epesè 10μm. Sepandan, 1235 mande pou plis egzak kontwòl rkwir akòz kontni Manganèz li yo (0.02 - 0.05%). Pifò manifaktirè batri prim kounye a pito 1235 pou pwodwi wo-sik-lavi.
Ki sa ki bon jan kalite tès yo kritik pou 1235 papye batri anvan chajman?
Tès pinhole lè l sèvi avèk 500V DC vòltaj asire mwens pase oswa egal a 1 domaj pou chak 10m ² nan papye 10μm. Tès rupture verifye konsistans elongasyon (± 2% varyasyon pakèt). Se epesè sifas kouch oksid mezire pa eddy aktyèl (20 - sib 50nm). Se lwil oliv rezidyèl woule chiffres pa GC-MS (<5mg/m²). Most importantly, foil samples undergo actual battery cell testing for 100 cycles to confirm electrochemical stability before bulk delivery.